Ericsson, M., Sandstrom, R., & Hagstrom, J. (2000, June). Fatigue of friction stir welded AlMgSi-alloy 6082. 2nd International Symposium.
Ericsson M, Sandstrom R and Hagstrom J. "Fatigue of friction stir welded AlMgSi-alloy 6082". 2nd International Symposium (Jun.2000).
Ericsson, M, Sandstrom, R and Hagstrom, J. "Fatigue of friction stir welded AlMgSi-alloy 6082". 2nd International Symposium (Jun.2000).
Ericsson M., Sandstrom R. and Hagstrom J.Fatigue of friction stir welded AlMgSi-alloy 6082. 2nd International Symposium. 2000 Jun; .
Ericsson, Sandstrom & Hagstrom 2000, 'Fatigue of friction stir welded AlMgSi-alloy 6082', 2nd International Symposium. Available from: https://www.twi-global.com/technical-knowledge/fsw-symposium-papers/FSWSymposia-200006-8Paper01.pdf.
Ericsson M, Sandstrom R, Hagstrom J. Fatigue of friction stir welded AlMgSi-alloy 6082. 2nd International Symposium. 2000;. https://www.twi-global.com/technical-knowledge/fsw-symposium-papers/FSWSymposia-200006-8Paper01.pdf.
Ericsson MM, Sandstrom RR, Hagstrom JJ. Fatigue of friction stir welded AlMgSi-alloy 6082. 2nd International Symposium. 2000 Jun;. https://www.twi-global.com/technical-knowledge/fsw-symposium-papers/FSWSymposia-200006-8Paper01.pdf.
Fatigue of friction stir welded AlMgSi-alloy 6082
- Ericsson M. ,
- Sandstrom R. and
- Hagstrom J.
- Ericsson M. ,
- Sandstrom R. and
- Hagstrom J.
June 2000
Links
Repository
Description
The tensile and fatigue strength of friction stir welds were determined for aluminium alloy 6082 in various temper conditions. Plate of 5.8 mm thickness, in both T6 and T4 conditions, was welded using a tool speed of 1000 rev/min and a welding speed of 350 mm/min. The welds in the T4 condition alloy were subjected to PWHT (185 deg.C for 5 h). The hardness, ultimate tensile strength, elongation and fatigue strength were determined using samples cut perpendicular to the welding direction. Fracture surfaces, and the microstructure of the parent materials and the welded joints, were studied by microscopy.
2nd International Symposium, 26-28 Jun 2000, Session 8, Paper 01